Small Refractory MGO Magnesium Oxide Ceramic Crucible for Lab Analysis

Small Refractory MGO Magnesium Oxide Ceramic Crucible for Lab Analysis
Product Details
We take 'Integrity Enterprise, Professional Technology, Technological Innovation' as the development idea, and strive to contribute more to the torch ceramic nozzle, transformer bushing, Ceramic for immersion heater industry. The more types of our business teams, the stronger our competitiveness to meet customer needs. Welcome all of the friends and customers to join us. We believe that product quality not only depends on technology and reliability, but also on mature design and perfect use functions. Thus far, our item associated with printer dtg a4 may be shown in most foreign nations as well as urban centers, which are sought after simply by targeted traffic.

The capacity of the crucible is 5 to 2000ml according to appearance, maximum capacity can be customized, and maximum size is 450mm. Under the general condition, the analyzed and fired substance is put into the crucible or a sagger and then put into analyzing or firing equipment to be heated. Heating and cooling speed is different according to the characteristics of the equipment and products. A raw material for manufacturing the crucible and the sagger is subjected to thermal expansion, and the crucible and the sagger are easily cracked if the heating or cooling speed is overhigh, so that the speed had better be low to prolong the service life of the crucible and the sagger. A corundum crucible contains 99.70% of corundum, has good high temperature insulation property and mechanical strength at the temperature of 1650 to 1700℃ in oxidizing atmosphere and reducing atmosphere, high heat conductivity and low thermal expansivity, does not react with air, water vapor, hydrogen, carbon monoxide and so on at the temperature of more than 1700℃, and has the short-term maximum service temperature of 1800℃.


Technical parameters:

Content: >99%

Density: 3.85g/cm3

Compressive strength: 2500MPa

Bending strength: 360MPa

Thermal shock resistance (thermal stability): good 

Maximum service temperature: 1800℃


On the basis of providing high-quality Small Refractory MGO Magnesium Oxide Ceramic Crucible for Lab Analysis, we strive to create higher benefits and greater value for customers with comprehensive and perfect services. We sincerely look forward to cooperate with global users and partners to seek common development. We will always adhere to the business philosophy of integrity, innovation, professionalism, and efficiency, and pursue the tenet of customer supremacy, quality first, and leading technology to create maximum value for customers!